| 布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 86,6 | 70,0 | 1037 | 78,5 | 55,0 | 599 | ||
| 86,3 | 69,5 | 1017 | 78,2 | 54,5 | 589 | ||
| 86,1 | 69,0 | 997 | 77,9 | 54,0 | 579 | ||
| 85,8 | 68,5 | 978 | 77,7 | 53,5 | 570 | ||
| 85,5 | 68,0 | 959 | 77,4 | 53,0 | 561 | ||
| 85,2 | 67,5 | 941 | 77.1 | 52,5 | 551 | ||
| 85,0 | 67,0 | 923 | 76,9 | 52,0 | 543 | ||
| 84,7 | 66,5 | 906 | 76,6 | 51,5 | 534 | ||
| 84,4 | 66,0 | 889 | 501 | 76,3 | 51,0 | 525 | |
| 84,1 | 65,5 | 872 | 494 | 76.1 | 50,5 | 517 | |
| 83,9 | 65,0 | 856 | 488 | 75,8 | 50,0 | 509 | |
| 83,6 | 64,5 | 840 | 481 | 75,5 | 49,5 | 501 | |
| 83,3 | 64,0 | 825 | 474 | 75,3 | 49,0 | 493 | |
| 83.1 | 63,5 | 810 | 468 | 75,0 | 48,5 | 485 | |
| 82,8 | 63,0 | 795 | 461 | 74,7 | 48,0 | 478 | |
| 82,5 | 62,5 | 780 | 455 | 74,5 | 47,5 | 470 | |
| 82,2 | 62,0 | 766 | 449 | 74,2 | 47,0 | 463 | |
| 82,0 | 61,5 | 752 | 442 | 73,9 | 46,5 | 456 | |
| 81,7 | 61,0 | 739 | 436 | 73,7 | 46,0 | 449 | |
| 81,4 | 60,5 | 726 | 430 | 73,4 | 45,5 | 443 | |
| 81,2 | 60,0 | 713 | 424 | 73,2 | 45,0 | 436 | |
| 80,9 | 59,5 | 700 | 418 | 72,9 | 44,5 | 429 | |
| 80,6 | 59,0 | 688 | 413 | 72,6 | 44,0 | 423 | |
| 80,3 | 58,5 | 676 | 407 | 72,4 | 43,5 | 417 | |
| 80.1 | 58,0 | 664 | 401 | 72.1 | 43,0 | 411 | |
| 79,8 | 57,5 | 653 | 396 | 71,8 | 42,5 | 405 | |
| 79,5 | 57,0 | 642 | 391 | 71,6 | 42,0 | 399 | |
| 79,3 | 56,5 | 631 | 385 | 71,3 | 41,5 | 393 | |
| 79,0 | 56,0 | 620 | 380 | 71.1 | 41.0 | 388 | |
| 78,7 | 55,5 | 609 | 375 | 70,8 | 40,5 | 382 | |
Tabelle fir d'Ëmrechnung vun der Härtewäert vun Eisenmetallmaterialien
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 370 | 70,5 | 40,0 | 377 | 269 | 28.0 | 274 | |
| 365 | 70,3 | 39,5 | 372 | 266 | 27,5 | 271 | |
| 360 | 70,0 | 39,0 | 367 | 263 | 27.0 | 268 | |
| 355 | 38,5 | 362 | 260 | 26,5 | 264 | ||
| 350 | 38,0 | 351 | 257 | 26.0 | 261 | ||
| 345 | 37,5 | 352 | 254 | 25,5 | 258 | ||
| 341 | 37,0 | 347 | 251 | 25,0 | 255 | ||
| 336 | 36,5 | 342 | 248 | 24,5 | 252 | ||
| 332 | 36,0 | 338 | 245 | 24.0 | 249 | ||
| 327 | 35,5 | 333 | 242 | 23,5 | 246 | ||
| 323 | 35,0 | 329 | 240 | 23.0 | 243 | ||
| 318 | 34,5 | 324 | 237 | 22,5 | 240 | ||
| 314 | 34,0 | 320 | 234 | 22.0 | 237 | ||
| 310 | 33,5 | 316 | 232 | 21,5 | 234 | ||
| 306 | 33,0 | 312 | 229 | 21.0 | 231 | ||
| 302 | 32,5 | 308 | 227 | 20,5 | 229 | ||
| 298 | 32,0 | 304 | 225 | 20.0 | 226 | ||
| 294 | 31,5 | 300 | 222 | 19,5 | 223 | ||
| 291 | 31.0 | 296 | 220 | 19.0 | 221 | ||
| 287 | 30,5 | 292 | 218 | 18,5 | 218 | ||
| 283 | 30.0 | 289 | 216 | 18.0 | 216 | ||
| 280 | 29,5 | 285 | 214 | 17,5 | 214 | ||
| 276 | 29.0 | 281 | 211 | 17.0 | 211 | ||
| 273 | 28,5 | 278 | |||||
Bemierkung:
1. Brinell-Härte: Si gëtt haaptsächlech benotzt fir d'Härte vu Gossstécker, Schmiedstécker, Net-Eisenmetalldeeler, waarmgewalzten Billets an geglühten Deeler ze moossen. De Miessberäich ass ≥HB450.
2. Rockwell-Härte: HRA gëtt haaptsächlech fir Prouwe mat héijer Härte benotzt, fir d'Uewerflächenhärte vu Materialien an Uewerflächen mat enger Härte méi héich wéi HRC67 ze moossen, wéi z. B. Hartmetall, Nitréierungsstol, etc. De Miessberäich ass HRA>70. HRC gëtt haaptsächlech benotzt fir d'Härte vu Stoldeeler (wéi z. B. Kuelestol, Werkzeugstol, Legierungsstol, etc.) no Ofkille oder Antléisst ze moossen. De Miessberäich ass HRC20~67.
3. Vickers-Härte: gëtt benotzt fir d'Härte vun dënnen Deeler an Stahlplackendeeler ze moossen, a kann och benotzt ginn fir d'Härte vun Uewerflächen gehärteten Deeler ze moossen, wéi z. B. Karburéieren, Zyanéieren an Nitréieren.